Die Forging High Speed Roller Cast Steel High Hardness For Roll Mill
Products:
die steel roller,high speed roller,cast steel roller,die steel roller shaft,high Cr roller
Products reference:
| Material | 4140,60CrMo,9Cr2Mo,90Cr3 |
| Forging equipment | 8000T Open die hydropress |
| Application |
Die steel roller is mainly used for high hardness roller mill |
| Melting process | EF+LF+VD |
| Production process |
Forging+heat treatment+rough machining+QT |
| Forging ratio |
≥3.5 |
| Applicable standard | ASTM,ASME,DIN,JIS,ISO,BS,API,EN |
| Executive standard | JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
| Certification authority | ISO9001:2008,BV,SGS, IST, UL,CTI |
| Delivery term |
Rough machining(N+T);finish machining(Q+T) |
|
Test equipment |
Spectrograph,UT device,tensile and impact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
| Service | Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
Custom properties
| Material elements | C | Si | Mn | P | S | Cr | Ni | Mo |
Others |
| 4140 | 0.38-0.43 | 0.15-0.35 | 0.60-0.90 | ≤0.035 | ≤0.040 | 0.80-1.10 | -- | 0.15-0.25 | - |
| 60CrMo | 0.55-0.65 | 0.17-0.30 | 0.450-0.80 | ≤0.020 | ≤0.015 | 0.50-0.80 | ≤0.25 | 0.20-0.40 | |
| 9Cr2Mo | 0.85-0.95 | 0.25-0.45 | 0.20-0.40 | ≤0.025 | ≤0.025 | 1.70-2.10 | ≤0.25 | 0.20-0.40 |
|
Mechanical property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Type Of notch |
Impact energy |
HBW |
| 4140 | Ø25 | 740~1000 | 450~850 | ≥12 | ≥25 | V | ≥40 | ≤250HBS |
Process procedure:
Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment
Commerce clause
| MOQ | 1PC |
| Max length | 10000MM |
| Delivery time | 30-60 days |
| Package | wood pallet,steel frame |
| Delivey term | FOB;CIF;CFR；DDU； |
| Payment term | T/T,LC |
| Type of shipping |
By ocean,air |
Keywords:
die steel has solidification crack,impact resistance,wear resistance advantages,common material is 4140,60CrMo,9Cr2Mo,90Cr3 high Cr materials.